410S rostfritt stålspole
Beskrivning
Specifikationer:
1. Standard: ASTM A240, JIS G4304, EN10088
2. Betyg: 200series&300serien&400serien
3. Tjocklek: 0,03 mm - 6,0 mm
4. Bredd: 8mm-600mm
5. Längd: som kundernas begäran
6. Yta: 2D,2B, BA, Mirror finished, N04, Hair Line, Matt finish, 6K, 8K
7.Teknik: kalldragen/kallvalsad/varmvalsad
Material:
| Typ | Kvalitet | Kvalitet | Kemisk komponent % | ||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | Övrig | |||
| Austenitisk | 201 | SUS201 | ≤0,15 | 16.00-18.00 | 3,50-5,50 | 5,50–7,50 | ≤0,060 | ≤0,030 | - | ≤1,00 | - | ≤0,25 | - |
| 202 | SUS202 | ≤0,15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ≤0,060 | ≤0,030 | ≤1,00 | - | ≤0,25 | – | ||
| 301 | 1,4310 | ≤0,15 | 16.00-18.00 | 6.00-8.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | ≤0,10 | - | |
| 304 | 1,4301 | ≤0,07 | 17.00-19.00 | 8.00-10.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 304L | 1,4307 | ≤0,030 | 18.00-20.00 | 8.00-10.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 304H | 1,4948 | 0,04-0,10 | 18.00-20.00 | 8.00-10.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 309 | 1,4828 | ≤0,20 | 22.00-24.00 | 12.00-15.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 309S | * | ≤0,08 | 22.00-24.00 | 12.00-15.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 310 | 1,4842 | ≤0,25 | 24.00-26.00 | 19.00-22.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 310S | * | ≤0,08 | 24.00-26.00 | 19.00-22.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 314 | 1,4841 | ≤0,25 | 23.00-26.00 | 19.00-22.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | 1.50-3.00 | - | - | - | |
| 316 | 1,4401 | ≤0,08 | 16.00-18.50 | 10.00-14.00 | ≤2,00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1,00 | - | - | - | |
| 316L | 1,4404 | ≤0,030 | 16.00-18.00 | 10.00-14.00 | ≤2,00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1,00 | - | - | - | |
| 316Ti | 1,4571 | ≤0,08 | 16.00-18.00 | 10.00-14.00 | ≤2,00 | ≤0,045 | ≤0,030 | 2.00-3.00 | ≤1,00 | - | 0,1 | Ti5(C+N)~0,70 | |
| 317 | * | ≤0,08 | 18.00-20.00 | 11.00-15.00 | ≤2,00 | ≤0,045 | ≤0,030 | 3.00-4.00 | ≤1,00 | - | 0,1 | - | |
| 317L | 1,4438 | ≤0,03 | 18.00-20.00 | 11.00-15.00 | ≤2,00 | ≤0,045 | ≤0,030 | 3.00-4.00 | ≤1,00 | - | 0,1 | - | |
| 321 | 1,4541 | ≤0,08 | 17.00-19.00 | 9.00-12.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Ti5(C+N)~0,70 | |
| 321H | * | 0,04-0,10 | 17.00-19.00 | 9.00-12.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Ti5(C+N)~0,70 | |
| 347 | 1,4550 | ≤0,08 | 17.00-19.00 | 9.00-12.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Nb > 10*C%-1,10 | |
| 347H | 1,494 | 0,04-0,10 | 17.00-19.00 | 9.00-12.00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Nb > 10*C%-1,10 | |
| Duplex | 2205 | S32205 | ≤0,03 | 22.0-23.0 | 4,5-6,5 | ≤2,00 | ≤0,030 | ≤0,020 | 3,0-3,5 | ≤1,00 | - | 0,14-0,20 | |
| 2507 | S32750 | ≤0,03 | 24,0-26,0 | 6,0-8,0 | ≤1,20 | ≤0,035 | ≤0,020 | 3,0-5,0 | ≤0,80 | 0,5 | 0,24-0,32 | ||
| Ferrit | 409 | S40900 | ≤0,03 | 10.50-11.70 | 0,5 | ≤1,00 | ≤0,040 | ≤0,020 | - | ≤1,00 | - | ≤0,030 | Ti6(C+N)~0,50 Nb:0,17 |
| 430 | 1Cr17 | ≤0,12 | 16.00-18.00 | - | ≤1,0 | ≤0,040 | ≤0,030 | - | ≤1,0 | - | - | - | |
| 444 | S44400 | ≤0,025 | 17.50-19.50 | 1 | ≤1,00 | ≤0,040 | ≤0,030 | 1,75-2,5 | ≤1,00 | - | 0,035 | Ti+Nb:0,2+4(C+N)~0,80 | |
| Martensit | 410 | 1Cr13 | 0,08-0,15 | 11.50-13.50 | 0,75 | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - |
| 410S | * | ≤0,080 | 11.50-13.50 | 0,6 | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 420 | 2Cr13 | ≥0,15 | 12.00-14.00 | - | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 420J2 | 3Cr13 | 0,26-0,35 | 12.00-14.00 | - | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - | |
| PH | 630 | 17-4PH | ≤0,07 | 15.00-17.50 | 3.00-5.00 | ≤1,00 | ≤0,035 | ≤0,030 | - | ≤1,00 | 3.00-5.00 | - | Nb 0,15-0,45 |
| 631 | 17-7PH | ≤0,09 | 16.00-18.00 | 6.50-7.50 | ≤1,00 | ≤0,035 | ≤0,030 | - | ≤1,00 | ≤0,50 | - | Al 0,75-1,50 | |
| 632 | 15-5PH | ≤0,09 | 14.00-16.00 | 3,50-5,50 | ≤1,00 | ≤0,040 | ≤0,030 | 2.00-3.00 | ≤1,00 | 2,5-4,5 | - | Al 0,75-1,50 | |
Grundläggande information
410s rostfritt stålspole, med bra korrosionsbeständighet och bearbetbarhet, det är ett stål för allmänt ändamål och skärverktygsstål.410S är ett slags stål som kan förbättra korrosionsbeständigheten och formbarheten hos 410-stål.410S är ett höghållfast stål som ytterligare kan förbättra korrosionsbeständigheten hos 410-stål.Den används för turbinblad och högtemperaturdelar.
• Specifikationer: AISI 410s, ASTM 410s
• Ytbehandlingar: Ba-yta, 2b-yta, No.1 (vit hud), 2D-yta, No.4 (frostad), HL (tråddragning), 8K-yta har utmärkt ytkvalitet
•Frästoleranser på tjocklek & planhet gäller. Ring JM Steel om du behöver specifika storlekar eller kornriktning.
410S Karakteristisk bearbetningsteknik
1D -- Ytan har diskontinuerlig granulär form, även känd som dimyta.
Bearbetningsteknik: varmvalsning + glödgning kulblästring betning + kallvalsning + glödgning betning.
2D - En lätt silvervit färg.
Bearbetningsteknik: varmvalsning + glödgning kulblästring betning + kallvalsning + glödgning betning.
2B -- Silvervit med bättre glans och planhet än en 2D-yta.
Bearbetningsteknik: varmvalsning + glödgning kulblästring betning + kallvalsning + glödgning betning + härdning och anlöpningsvalsning.
Ba - Utmärkt ytglans, hög reflektivitet, som en spegelyta.
Bearbetningsteknik: varmvalsning + glödgning kulblästring betning + kallvalsning + glödgning betning + ytpolering + härdnings- och anlöpningsvalsning.
Nr 3 -- Bra glans, grovkornig yta.
Bearbetningsteknik: polering och härdningsvalsning för 2D eller 2B med 100~120 slipmaterial (JIS R6002).
Nr 4 -- Bra glans, fina linjer på ytan.
Bearbetningsprocess: polering och härdningsvalsning för 2D eller 2B med 150~180 slipmaterial (JIS R6002).
HL -- Silvergrå med hårstrån.
Bearbetningsteknik: 2D-produkter eller 2B-produkter med lämplig granularitet av slipmaterial för polering av ytan är ett kontinuerligt slipkorn.
MIRRO -- Speglande.
Bearbetningsteknik: 2D-produkter eller 2B-produkter med lämplig granularitet av slipmaterialet slipning och polering till spegeleffekt.